STUDI PENGGUNAAN ASBUTON PADA CAMPURAN ASPAL PANAS ASPHALT CONCRETE-WEARING COURSE (AC-WC)

Teguh Muhammad Assiddiqie; Ade Rizki Nurmayadi; Dicky Nurmayadi

doi:10.36423/jitsi.v4i2.2108

Authors

Teguh Muhammad Assiddiqie Universitas Perjuangan
Ade Rizki Nurmayadi Fakultas Teknik, Universitas Perjuangan Tasikmalaya
Dicky Nurmayadi Fakultas Teknik, Universitas Perjuangan Tasikmalaya

DOI:

https://doi.org/10.36423/jitsi.v4i2.2108

Keywords:

Asphalt Concrete – Wearing Course (AC-WC), Asbuton Lawele Granullar Asphalt (LGA), Marshall Test, Marshall Immersion, Marshall Quotient (MQ)

Abstract

Abstract— Based on the Regulation of the Minister of PUPR No.18/PRT/M/2018 concerning the use of buton asphalt for road construction and preservation, further research was carried out to understand the characteristics of the Asphalt Concrete - Wearing Course (AC-WC) mixture. This study used Asbuton LGA type 50/30 with percentages of 3%, 6%, and 9% of the total weight of the mixture. There are a total of 42 test pieces, consisting of 30 for PKAO and 12 for KAO. The results showed that the mixture of AC-WC with 3% Asbuton LGA produced KAO of 5.7%, VIM Value 3.77%, VMA Value 14.96%, VFB Value 74.79%, Marshall Stability Value 1,366 Kg, Flow Value 3.15 mm, Marshall Quetient Value (MQ) 434 Kg/mm, and Immersion Value 90.33%. With the addition of 6% Asbuton LGA, KAO becomes 6%, VIM Value 4.87%, VMA Value 15.21%, VFB Value 67.97%, Marshall Stability Value 1,567 Kg, Flow Value 3.60 mm, MQ Value 435 Kg/mm, and Immersion Value 91.23%. The addition of 9% of Asbuton LGA resulted in a KAO of 6.3%, a VIM value of 7.11%, a VMA value of 18.43%, a VFB value of 61.43%, a Marshall Stability Value of 2,250 Kg, a Flow Value of 4.90 mm, an MQ Value of 459 Kg/mm, and an Immersion Value of 54.85%. The percentage of LGA Asbutone of 6% in the AC-WC mixture showed an increase in the Marshall stability value and Marshall immersion.

Keywords — Asphalt Concrete – Wearing Course (AC-WC), Asbuton Lawele Granullar Asphalt (LGA), Marshall Test, Marshall Immersion, Marshall Quotient (MQ)

Abstrak— Berdasarkan Peraturan Menteri PUPR No.18/PRT/M/2018 mengenai penggunaan aspal buton untuk pembangunan dan preservasi jalan, dilakukan penelitian lanjutan untuk memahami karakteristik campuran Asphalt Concrete - Wearing Course (AC-WC). Penelitian ini menggunakan Asbuton LGA tipe 50/30 dengan persentase 3%, 6%, dan 9% dari total berat campuran. Total terdapat 42 benda uji, terdiri dari 30 untuk PKAO dan 12 untuk KAO. Hasil penelitian menunjukkan bahwa campuran AC-WC dengan 3% Asbuton LGA menghasilkan KAO sebesar 5,7%, Nilai VIM 3,77%, Nilai VMA 14,96%, Nilai VFB 74,79%, Nilai Stabilitas Marshall 1.366 Kg, Nilai Flow 3,15 mm, Nilai Marshall Quetient (MQ) 434 Kg/mm, dan Nilai Immersion 90,33%. Dengan penambahan 6% Asbuton LGA, KAO menjadi 6%, Nilai VIM 4,87%, Nilai VMA 15,21%, Nilai VFB 67,97%, Nilai Stabilitas Marshall 1.567 Kg, Nilai Flow 3,60 mm, Nilai MQ 435 Kg/mm, dan Nilai Immersion 91,23%. Penambahan 9% Asbuton LGA menghasilkan KAO sebesar 6,3%, Nilai VIM 7,11%, Nilai VMA 18,43%, Nilai VFB 61,43%, Nilai Stabilitas Marshall 2.250 Kg, Nilai Flow 4,90 mm, Nilai MQ 459 Kg/mm, dan Nilai Immersion 54,85%. Persentase Asbuton LGA sebesar 6% pada campuran AC-WC menunjukkan peningkatan nilai stabilitas Marshall dan perendaman Marshall.

Kata kunci — Asphalt Concrete – Wearing Course (AC-WC). Asbuton Lawele Granullar Asphalt (LGA), Marshall Test, Marshall Perendaman, Marshall Quotient (MQ)

References

Abdillah, N., & Muhabbah, Z. (2019). Pemanfaatan Limbah Sandblasting Pasir Silika Sebagai Bahan Pengganti Agregat Halus Untuk Campuran Beton. Jurnal Unitek, 12(1), 10–16.

Al Mahbubi, M. (2019). Studi Penggunaan Agregat Buatan Berbahan Dasar Fly Ash Pada Agregat Kasar Terhadap Perkerasan Lentur Untuk Pengurangan Penggunaan Agregat Alam. Institut Teknologi Sepuluh Nopember.

Asyiah, S., Intari, D. E., Purnaditya, N. P., Bethary, R. T., Fathonah, W., & Anggini, N. (2021). Pengaruh Perendaman Cairan Kimia (Disenfektan) Terhadap Karakteristik Asphalt Concrete-Wearing Course (AC-WC). Fondasi: Jurnal Teknik Sipil, 10(2), 179–190.

Dermawan, H., Olivia, M., & Djauhari, Z. (2022). Sifat Fisik dan Mekanis Beton Sekat Kanal High Volume Fly Ash (HVFA) di Lingkungan Gambut. JURNAL TEKNIK, 16(1), 23–31.

Giroth, M. I., Sendow, T. K., & Palenewen, S. C. N. (2019). PERBANDINGAN KRITERIA MARSHALL PADA CAMPURAN ASPAL PANAS (AC-WC) YANG MENGGUNAKAN ASBUTON MODIFIKASI (RETONA BLEND) DENGAN ASPAL PENETRASI 60/70 (Studi Kasus: Penggunaan Material Agregat Dari Kema Sulawesi Utara). Jurnal Sipil Statik, 7(11), 1547–1556.

Kafabihi, A., & Wedyantadji, B. (2020). Penggunaan aspal buton pada campuran AC-WC (asphalt concrete-wearing course). Student Journal Gelagar, 2(2), 36–44.

Lendra, L., Gawei, A. B. P., & Sintani, L. (2022). Analisis Konsumsi Energi dan Emisi Gas Rumah Kaca Pada Pekerjaan Konstruksi Jalan Dengan Perkerasan Lentur dan Perkerasan Kaku. Jurnal Reka Lingkungan, 10(3), 201–211.

Pinangkaan, V., Sompie, T. P. F., & Sudarno, S. (2022). Analisis Perbandingan Karakteristik antara AC-WC Asbuton dengan Cold Paving Hot Mix Asbuton (CPHMA). Semesta Teknika, 25(1), 60–70.

Putra, F. Y. E. (2020). Pemanfaatan Limbah Polyethylene Terepthalate (PET) dengan Reclaimed Asphalt Pavement (RAP) Pada Pembuatan Laston WC. Jurnal Rekats, 8(5), 1–8.

Putra, N. E., eka Putri, E., & Purnawan, P. (2022). DURABILITAS CAMPURAN LASTON AC-WC DI SUBSTITUSI CAMPURAN LIMBAH PLASTIK LDPE, PP, PS. Jurnal Teknik Sipil, 11(2), 141–147.

Rachman, D. N., Riwayati, S., Sirait, D. R., & Arfan, M. (2022). Penambahan Fly Ash Batu Bara Pltu Sebagai Filler Aspal Ac Wc. Bearing: Jurnal Penelitian Dan Kajian Teknik Sipil, 7(4), 207–214.

Rasul, R. F., & Sari, Y. A. (2022). Pengaruh Penambahan Limbah Serbuk PVC Pada Campuran Laston Lapis Aus. Jurnal Ilmiah Rekayasa Sipil, 19(2), 127–135.

Rendra, A., & Mudjanarko, S. W. (2019). Analisis Perbandingan Flexible Pavemenet As Buton Pra Campur dengan Plastik HDPE untuk Lapisan AC WC. Narotama University Press.

Rifai, A. I., Hafidh, M., Isradi, M., & Prasetijo, J. (2023). The ANALISIS KINERJA COLD PAVING HOT MIX ASBUTON DENGAN FILLER PORTLAND CEMENT TERHADAP INTENSITAS RENDAMAN. Teknisia, 28(1), 25–34.

Rohma, I. W., Supriyanto, B., & Rahardjo, B. (2023). Analisis Kinerja Campuran Perkerasan Asphalt Concrete-Wearing Course (AC-WC) Menggunakan Bahan Tambah Asbuton B 50/30 Terhadap Parameter Marshall. Media Teknik Sipil, 21(1), 32–38.

Sumiati, S., Mahmuda, M., & Puryanto, P. (2019). Keunggulan asbuton pracampuran dan aspal shell pada campuran aspal beton (AC-BC). Jurnal Poli-Teknologi, 18(1).

Talamati, B. H., & Lestari, M. I. (2023). Pengaruh Kehilangan Gradasi Halus pada Spesifikasi Ream Pengujian Cantabro. Jurnal Vokasi Sains Dan Teknologi, 3(1), 1–6.

Van Gobel, F. M. (2019). Nilai kuat tekan beton pada slump beton tertentu. Radial, 5(1), 22–33.